Physical and Electrical Characteristics of Carbon Nanotube Network Field-Effect Transistors Synthesized by Alcohol Catalytic Chemical Vapor Deposition
Figure 3
Cross-sectional view of SEM morphology of CNTNs formed on the SiO2/n-type Si(100) stacked substrate. Various plane views were also shown in the inset of figure. The growth conditions were carried out at (a) 750, (b) 700, and (c) 650°C in the alcohol ambient for 10 min, and the partial pressure was achieved in 10 Torr. A Co/Mo acetate was premixed at Co : Mo = 0.1 : 0.1 wt% and dissolved in ethanol with sonication for 8 hours.
