Physical and Electrical Characteristics of Carbon Nanotube Network Field-Effect Transistors Synthesized by Alcohol Catalytic Chemical Vapor Deposition
Figure 4
Plane view of TEM morphology of CNTNs was formed on the SiO2/n-type Si(100) stacked substrate. The growth conditions were carried out at 750°C in the alcohol ambient for 10 min, and the partial pressure was achieved in 10 Torr. A Co/Mo acetate was premixed at Co : Mo = 0.1 : 0.1 wt% and dissolved in ethanol with sonication for 8 hours.