Design Modifications in Electrospinning Setup for Advanced Applications
Figure 8
(a) The electrospinning setup for the fabrication of aligned TiO2 fibers. The increase in the alignment of the fiber was observed with the increase in the rotation speed of the disc collector. The speed of the disc was increased from (b) 800, (c) 1000 to (d) 2000 rpm to obtain aligned fibers. The electrospinning was performed at flow rate of 0.1 mL/h with the applied electric field strength of 1 kV/cm.
