Synthesis of Nanocrystalline WC Single-Phase Refractory via Mechanical Milling
Table 2
Crystalline size and mean strain of synthesized WC.
| Time (hr) | | crystalline size (nm) | mean strain (%) | Determination Method | a | b |
| W–C mixture |
| 75 | — | — | 69.21 | 0.71 | Scherrer | 100 | 0.018 | 0.004 | 39.60 | 1.80 | W–H | 150 | 0.025 | 0.007 | 20.09 | 2.51 | W–H |
| W–C–WC mixture |
| 75 | 0.015 | 0.003 | 46.20 | 1.50 | W–H | 100 | 0.020 | 0.005 | 30.13 | 1.97 | W–H | 150 | 0.031 | 0.017 | 8.35 | 3.06 | W–H |
| W–C–Al2O3 Mixture |
| 150 | 0.026 | 0.008 | 18.00 | 2.57 | W–H |
|
|