Research Article
Microstructural Study of ZnO Nanostructures by Rietveld Analysis
Table 2
Results of Rietveld refinement.
| Sample | Rp | Rwp | GofF | Lattice parameters | Preferred orientation | Size parameters | B overall (Å2) | Oxygen | a (Å) | c (Å) | c/a | G1 (101) | Vol. oriented % | Y | S (Z) |
| Z1 | 15.5 | 12.2 | 0.8 | 3.247 | 5.203 | 1.602 | 0.857 | 8.9 | 0.025 | 0.471 | 1.64 | 0.374 | Z2 | 17.6 | 12.8 | 0.8 | 3.251 | 5.209 | 1.602 | 0.828 | 10.9 | 0.021 | 0.465 | 1.43 | 0.375 | Z3 | 21.2 | 15.0 | 0.9 | 3.250 | 5.206 | 1.602 | 0.830 | 10.5 | 0.026 | 0.695 | 2.09 | 0.370 | Z4 | 50.7 | 28.2 | 0.8 | 3.254 | 5.212 | 1.602 | 0.730 | 18.0 | 0.369 | -5.20 | 2.37 | 0.367 | Z5 | 17.0 | 12.6 | 0.9 | 3.252 | 5.211 | 1.602 | 0.821 | 11.3 | 0.038 | 0.137 | 1.04 | 0.374 | Z6 | 16.6 | 12.9 | 0.9 | 3.251 | 5.209 | 1.602 | 0.816 | 11.7 | 0.041 | 0.116 | 1.47 | 0.375 | Z7 | 12.6 | 10.7 | 1.0 | 3.252 | 5.212 | 1.602 | 0.861 | 8.6 | 0.031 | 0.414 | 0.65 | 0.378 | Z8 | 14.3 | 12.1 | 0.9 | 3.251 | 5.212 | 1.603 | 0.922 | 4.7 | 0.025 | 0.576 | 1.11 | 0.370 | Z9 | 35.0 | 22.6 | 0.9 | 3.249 | 5.205 | 1.602 | 0.799 | 12.9 | 0.045 | 0.397 | 2.30 | 0.373 | Z10 | 27.9 | 19.1 | 0.9 | 3.250 | 5.208 | 1.602 | 0.801 | 12.7 | 0.038 | 0.217 | 1.66 | 0.369 | Z11 | 23.6 | 17.4 | 1.2 | 3.251 | 5.210 | 1.602 | 0.778 | 14.4 | 0.036 | 0.152 | 1.56 | 0.376 | Z12 | 37.5 | 23.8 | 0.8 | 3.245 | 5.198 | 1.602 | 0.762 | 15.5 | 0.023 | 0.625 | 2.70 | 0.364 | Z13 | 29.1 | 20.0 | 0.9 | 3.251 | 5.208 | 1.602 | 0.899 | 6.1 | 0.019 | 0.765 | 2.30 | 0.372 | Z14 | 32.8 | 21.5 | 0.9 | 3.243 | 5.196 | 1.602 | 0.809 | 12.2 | 0.020 | 0.543 | 2.03 | 0.372 |
|
|