Effect of Low-Frequency Alternative-Current Magnetic Susceptibility in Thin Films
Table 1
Maximum alternative-current magnetic susceptibility and optimal frequency at various thicknesses and temperatures.
| NiFe thickness | Room temperature of maximum | Post-annealed 150°C-1 hr of maximum | Post-annealed 250°C-1 hr of maximum | Highest corresponding optimal resonance frequency (Hz) |
| 300 Å | 0.172299 | 0.212215 | 0.85171 | 30 Hz | 500 Å | 0.661307 | 2.148086 | 2.456315 | 250 Hz | 700 Å | 1.194991 | 2.344501 | 2.541269 | 250 Hz | 1000 Å | 1.360231 | 2.668716 | 3.456921 | 500 Hz |
|
|