<i>In Vitro</i> Degradation of PHBV Scaffolds and nHA/PHBV Composite Scaffolds Containing Hydroxyapatite Nanoparticles for Bone Tissue Engineering

<table>(a) Weight loss of PHBV scaffolds after  <i>in vitro </i>degradation for 6 weeks: (A) 78% porosity; (B) 88% porosity. (b) Weight loss of PHBV scaffold (▪) and HA/PHBV scaffold with 10% HA (<span style="font-family:monospace">▴</span>) after <i>in vitro</i> degradation for 6 weeks.</table>

Journal of Nanomaterials

fig8

Figure 8

Figure 8: <i>In Vitro</i> Degradation of PHBV Scaffolds and nHA/PHBV Composite Scaffolds Containing Hydroxyapatite Nanoparticles for Bone Tissue Engineering 

Figure 8 | In Vitro Degradation of PHBV Scaffolds and nHA/PHBV Composite Scaffolds Containing Hydroxyapatite Nanoparticles for Bone Tissue Engineering 