In Vitro Degradation of PHBV Scaffolds and nHA/PHBV Composite Scaffolds Containing Hydroxyapatite Nanoparticles for Bone Tissue Engineering

Table 2

Compressive modulus of PHBV scaffolds with different polymer concentration.

Polymer concentration	Compressive modulus (MPa)
5%	0.3±0.22
7.5%	1.1±0.61
10%	3.0±0.9
12.5%	5.0±0.8