Dense and Cellular Zirconia Produced by Gel Casting with Agar: Preparation and High Temperature Characterization

<table class="table-group" id="tab4"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr class="thead"><td align="left">Sample</td><td align="center">Modulus of elasticity (GPa)</td><td align="center">Modulus of rupture (MPa)</td><td align="center">Maximum strain (%)</td></tr><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td align="left">E46 porous </td><td align="center">6.4</td><td align="center">22.9</td><td align="center">3.4</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Results of high temperature (1500°C) bending test on porous sample.

Journal of Nanomaterials

tab4

Table 4

Table 4: Dense and Cellular Zirconia Produced by Gel Casting with Agar: Preparation and High Temperature Characterization 