Electrodeposition, Characterization, and Corrosion Stability of Nanostructured Anodic Oxides on New Ti-15Zr-5Nb Alloy Surface
Figure 5
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.