Liquid Phase Plasma Synthesis of Iron Oxide/Carbon Composite as Dielectric Material for Capacitor

Table 2

Physical properties and specific capacitance of the iron oxide/AC composite synthesized with different LPP process times.

LPP process time	BET [m^2/g]	Total pore volume [cm^3/g]	Specific capacitance [F/g]
Bare YP-50F	1712.6	0.8294	13.96
15 min	1523.9	0.7367	13.48
30 min	1488.3	0.7191	14.87
45 min	1447.5	0.6983	14.32
60 min	1403.5	0.6806	12.93