Research Article
Fabrication and
In Vitro
Evaluation of Nanosized Hydroxyapatite/Chitosan-Based Tissue Engineering Scaffolds
Table 1
The density, porosity, pore type, and compressive modulus of the scaffolds.
Scaffolds
Density
Porosity
Pore
Compressive modulus
(w/v)
(g/cm
3
)
(%)
Type
(MPa)
Chitosan
0.1783
88
Open
10%
HA/chitosan
0.2918
82
Open