Synthesis and Characterization of Nanostructured Nickel Diselenide NiSe<sub>2</sub> from the Decomposition of Nickel Acetate, (CH<sub>3</sub>CO<sub>2</sub>)<sub>2</sub>Ni

<table>X-ray powder diffraction pattern of NiSe<sub>2</sub> particles. The reaction was maintained at 150°C and the product was analysed after 20 hours and 150 hours.</table>

Journal of Nanomaterials

fig1

Figure 1

Figure 1: Synthesis and Characterization of Nanostructured Nickel Diselenide NiSe<sub>2</sub> from the Decomposition of Nickel Acetate, (CH<sub>3</sub>CO<sub>2</sub>)<sub>2</sub>Ni 

Journal of Nanomaterials

Synthesis and Characterization of Nanostructured Nickel Diselenide NiSe2 from the Decomposition of Nickel Acetate, (CH3CO2)2Ni

Figure 1

Synthesis and Characterization of Nanostructured Nickel Diselenide NiSe₂ from the Decomposition of Nickel Acetate, (CH₃CO₂)₂Ni