Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups
Figure 4
AFM topographic images obtained using the intermittent contact mode of PSt60%-b-PDEAEM40% thin films prepared from a 1% w/w toluene solution over mica substrate as a function of spin coating velocity: (a) 2000 rpm; (b) 5000 rpm; and (c) 8000 rpm.