Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups

<div>AFM topographic images obtained using the intermittent contact mode of PSt60%-b-PDEAEM40% thin films prepared from a 1% w/w benzene solution over mica substrate at a spinning velocity of 5000 rpm: (a) directly after spin coating (25°C) and after annealing in vacuum (10 torr) at 40°C for (b) 36 h and (c) 48 h.</div>

Journal of Nanomaterials

fig5

Figure 5

Figure 5: Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups

Figure 5 | Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups 