Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups

<div>AFM topographic images obtained using the intermittent contact mode of PSt60%-b-PDEAEM40% thin films prepared from a 1% w/w toluene solution over mica substrate at a spinning velocity of 2000 rpm: (a) directly after spin coating (25°C) and after thermal annealing in vacuum (10 torr, 170°C) for (b) 120 h and (c) 138 h.</div>

Journal of Nanomaterials

fig9

Figure 9

Figure 9: Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups

Figure 9 | Equilibrium and Nonequilibrium Nanoscale Ordering of Polystyrene-b-poly(N,N′-diethylaminoethyl methacrylate), a Block Copolymer Carrying Tertiary Amine Functional Groups 