Synergistic Effect of Nanosilica Aerogel with Phosphorus Flame Retardants on Improving Flame Retardancy and Leaching Resistance of Wood
Table 2
Mass variety of different stage for untreated and treated poplar wood.
| |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
: weight of untreated wood. : weight of treated wood after impregnation experiment. : weight of treated wood after leaching test. bWPG (weight percent gain) = . cRL (average turnover rate) = . dERL was the average turnover rate of untreated wood. eRSFR (rest loading efficiency) = WPG − RL + ERL. fLRV (leaching resistance value) = RSFR/WPG. |