Synthesis, Characteristics, and Material Properties Dataset of Bi:DyIG-Oxide Garnet-Type Nanocomposites
Table 4
Dataset obtained from the annealing study of Bi2Dy1Fe4.3Ga0.7O12:Bi2O3 garnet-oxide composite films (having 17 vol.% of excess bismuth oxide) prepared on GGG substrates and the corresponding optical/MO properties measured at 532 nm and 635 nm.
Annealing temperature (°C)
Annealing process duration (min)
Properties measured at 532 nm
Properties measured at 635 nm
Specific Faraday rotation (deg/µm)
Absorption coefficients (cm−1)
MO figure of merit (deg)
Specific Faraday rotation (deg/µm)
Absorption coefficients (cm−1)
MO figure of merit (deg)
550
<1
NA
NC
NC
NC
NC
NC
15
NA
NC
NC
NC
NC
NC
22
0.63
9040
1.39
0.033
1458
0.50
27
7.2
5997
24
2.062
1130
36.49
30
4.23
8331
10.15
0.986
1473
13.38
45
5.65
6736
16.77
1.733
1484
23.35
60
6.71
8563
15.67
1.828
2769
13.20
90
6.35
7732
16.42
1.63
2153
15.14
560
4
NA
NC
NC
NC
NC
NC
7
3.60
8201
8.78
NC
NC
NC
12
7.04
6950
20.25
2.019
1700
23.75
15
6.9
6332
21.8
2.138
1382
30.94
22
7.07
6145
23.01
2.062
1365
30.21
26
6.51
8201
15.87
1.8
2572
13.99
30
6.38
7720
16.52
1.81
2162
16.74
45
7.31
6477
22.57
1.938
1449
26.75
52
7.07
8125
17.40
2.004
3337
12.01
60
6.45
9361
13.78
1.828
2347
15.57
90
6.97
7232
19.27
NC
NC
NC
570
1
2.9
8857
6.53
0.381
1867
4.08
2
7.03
5950
23.63
1.88
1097
34.27
4
7.02
6332
22.17
2.128
1021
41.60
6
7.1
9315
15.25
2.119
2922
14.50
8
7.56
10353
14.60
2.168
3519
12.32
9
6.98
8956
15.58
1.95
3213
12.13
12
7.5
11428
13.12
2.076
4131
10.05
Not annealed or Faraday rotation was below detection limit. NC: not characterized.