Synthesis, Characteristics, and Material Properties Dataset of Bi:DyIG-Oxide Garnet-Type Nanocomposites
Table 5
Dataset obtained from the annealing study of Bi2Dy1Fe4.3Ga0.7O12:Bi2O3 garnet-oxide composite films (having 17 vol.% of excess bismuth oxide) prepared on glass (Corning 1737) substrates and the corresponding optical/MO properties measured at 532 nm and 635 nm.
Annealing temperature (°C)
Annealing process duration (min)
Properties measured at 532 nm
Properties measured at 635 nm
Specific Faraday rotation (deg/µm)
Absorption coefficients (cm−1)
MO figure of merit (deg)
Specific Faraday rotation (deg/µm)
Absorption coefficients (cm−1)
MO figure of merit (deg)
550
<1
NA
NC
NC
NC
NC
NC
13
NA
NC
NC
NC
NC
NC
15
5.85
7564
15.46
NC
NC
NC
22
6.42
7221
17.78
2.024
1765
24.08
27
6.52
6671
19.54
2.41
1588
28.90
30
6.85
7072
19.37
2.35
1830
24.46
45
7.04
7495
18.78
2.395
2091
21.82
60
6.82
7495
18.19
2.343
1867
23.90
90
6.47
7228
17.90
2.31
1828
24.07
560
4
NA
NC
NC
NC
NC
NC
7
6.28
8209
15.30
NC
NC
NC
12
6.54
7942
16.46
2.34
2026
23.09
15
6.74
8163
16.51
2.071
2082
19.89
22
6.57
7911
16.60
2.195
1857
23.64
26
6.74
7682
17.55
2.08
1943
21.41
30
7.2
6568
21.93
2.247
1941
23.15
45
6.76
7858
17.20
2.73
2103
25.96
52
6.67
7949
16.78
2.185
2151
20.32
60
7.1
6027
23.56
2.219
1821
24.37
570
1
6.54
7873
16.61
2.07
2145
19.30
2
6.21
8167
15.20
2.257
2119
21.30
4
6.65
8068
16.48
2.23
2214
20.15
8
7
6881
20.35
2.267
1903
23.83
12
6.96
8064
17.26
2.295
2532
18.13
Not annealed or Faraday rotation was below detection limit. NC: not characterized.