Effect of Hydrochloric Acid Concentration on Morphology of Polyaniline Nanofibers Synthesized by Rapid Mixing Polymerization

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td align="left">APS/Ani molar ratio</td><td align="center">1/4</td><td align="center">1/1</td><td align="center">4/1</td></tr><tr><td align="center" colspan="4"><hr/></td></tr><tr><td align="left">Conductivity (S⋅cm<sup>−1</sup>)</td><td align="center">0.6</td><td align="center">0.18</td><td align="center">0.04</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

The electrical conductivity of PANI nanofibers at different APS/Ani molar ratio.

Journal of Nanomaterials

tab3

Table 3

Table 3: Effect of Hydrochloric Acid Concentration on Morphology of Polyaniline Nanofibers Synthesized by Rapid Mixing Polymerization 