| Wavenumber (cm−1) | IR bands assignment | PDMS layer | Ag:HAP-PDMS layer |
| 490 | — | [20–23], Figure 4 | 498, 512, 543, 550 | — | [24, 25], Figure 5(a) | 562, 590, 602, 611 | — | P-O bending vibrations in tetrahedron in crystalline HAP [20–23, 26–35], Figure 5(a) | 620 | asymmetrical stretching vibration [36], Figure 3 | — | 695 | — | Crystallinity of SiO2 type materials [37], Figure 4 | 780 | — | Si-O-P vibration [38], Figure 5(c) | 784 | Si-C stretching vibration [36], Figure 3 | — | 814, 816, 817.5 | — | Si-O-Si bonds [27, 28], Figure 5(c) | 828 | — | Si-O-Ag [39, 40], Figure 5(d) | 860 | Si-CH3 rocking vibration [36], Figure 3 | — | 862 | — | Si-O, Si-C vibrations [28], Figure 5(e) | 870 | — | vibrations [20, 30, 41], Figure 5(e) | 877 | — | ions [32, 34, 42, 43], Figure 5(e) | 889 | Si-O bending vibration [37, 44], Figure 3 | — |
925, 945, 975 | — | P-O vibrations in group [20–23, 26–30, 45], Figure 5(b) | 1004, 1071 | Si-O-Si vibrations [36], Figure 3 | — | 1000, 1044, 1067, 1085 | — | [20–23, 26–35], Figure 5(b) | 1140 | — | Si-O vibrations [9, 37, 44], Figure 4 | 1152 | Si-O vibrations [9, 37, 44], Figure 3 | — | 1254, 1400 | CH3 vibrations in Si=CH3 group [36], Figure 3 | CH3 vibrations in Si=CH3 group [36], Figure 4 | 1650 | H2O, OH, Si-OH [46], Figure 3 | H2O, OH, Si-OH [46], Figure 4 | 2912, 2964 | C-H vibrations [36], Figure 3 | — |
|
|