In Vitro Biological Evaluation of Electrospun Polycaprolactone/Gelatine Nanofibrous Scaffold for Tissue Engineering

Table 1

Processing parameters and average fiber diameter of PCL and PCL/Ge nanofibrous scaffolds. Solution concentration, electric field, flow rate, and distance between tip and collector were kept constant at 14% w/v, 15 kV, 1 mL/h, and 10 cm. All diameters are presented as mean ± SD ().

Polymer	Weight ratio of PCL : Ge	Temperature (°C)	Humidity (%)	Average fiber diameter (nm)
PCL	—	21.9	50	88.02 ± 27.83
PCL/Ge	85 : 15	21.4	52	143.39 ± 28.60
PCL/Ge	70 : 30	23.1	50	155.60 ± 41.13
PCL/Ge	50 : 50	23.1	50	219.22 ± 87.93