In Situ Synthesis of Reduced Graphene Oxide-Reinforced Silicone-Acrylate Resin Composite Films Applied in Erosion Resistance

Table 1

The mechanical properties of the polymer composite film measured by the bulge test.

Loading (wt%)	Biaxial modulus (GPa)	Young’s modulus (GPa)	Residual stress (MPa)	Yielded stress (MPa)	(N/m)
0	0.08	0.05	4.6	8.2	5.5
0.27	0.13	0.07	10.3	14.8	6.1
1.10	0.25	0.14	10.5	24.1	11.4
1.93	0.20	0.11	12.2	22.7	12.3