Effect of Processing on Mechanically Alloyed and Spark Plasma Sintered Al-Al2O3 Nanocomposites
Table 4
Hardness of aluminum nanocomposites consolidated by SPS.
| Composite | (deg./min) | (MPa) | (°C) | Time (min) | HV (MPa) | Ref. |
| Al-15 vol.% Al2O3 | 200 | 50 | 550° | 5 | 923.9 | This work | Al-15 vol.% Al2O3 | 200 | 50 | 550° | 20 | 821.9 | This work | Al-10 vol.% Al2O3 | 200 | 50 | 550° | 5 | 1463.3 | This work | Al-10 vol.% Al2O3 | 200 | 50 | 550° | 20 | 1309.7 | This work | Al-2 vol.% Al2O3 | 200 | 50 | 550° | 5 | 1113.6 | This work | Al-2 vol.% Al2O3 | 200 | 50 | 550° | 20 | 1098.0 | This work | Pure Al BM 24 h | 200 | 50 | 550° | 5 | 837.8 | This work | Pure Al BM 24 h | 200 | 50 | 550° | 20 | 421.0 | This work | Pure Al | 200 | 50 | 550° | 5 | 369.3 | This work | Pure Al | 200 | 50 | 550° | 20 | 326.3 | This work | Pure Al | 200 | 50 | 600 | 10 | 313 | [15] | Al-1 wt.% SiC | 200 | 50 | 600 | 10 | 1080 | [15] | Al-5 wt.% SiC | 200 | 50 | 600 | 10 | 928 | [15] | Al-10 wt.% SiC | 200 | 50 | 600 | 10 | 1715.3 | [15] | Al5083 | 300 | 50 | 500 | 3 | 1480 | [39] | Al5083-10 wt.% SiC | 300 | 50 | 500 | 3 | 2500 | [39] | Al2124 | 100 | 35 | 500 | 20 | 1102.4 | [46] | Al2124 + 1 wt.% CNTs | 100 | 35 | 500 | 20 | 1181.9 | [47] | Al6061 | 100 | 35 | 450 | 20 | 660 | [47] | Al6061 + 1 wt.% CNTs | 100 | 35 | 450 | 20 | 710 | [47] | Al-7Si-0.3Mg | 100 | 35 | 500 | 20 | 630 | [48] | Al-7Si-0.3Mg + 0.5 wt.% CNTs | 100 | 35 | 500 | 20 | 680 | [48] | Al-12Si-0.3Mg | 100 | 35 | 500 | 20 | 680 | [48] | Al-12Si-0.3Mg + 0.5 wt.% CNTs | 100 | 35 | 500 | 20 | 830 | [48] | Al-7Si-0.3Mg | 100 | 35 | 500 | 20 | 630 | [33] | Al-7Si-0.3Mg + 5 wt.% SiC | 100 | 35 | 500 | 20 | 710 | [33] | Al-7Si-0.3Mg + 12 wt.% SiC | 100 | 35 | 500 | 20 | 750 | [33] | Al-7Si-0.3Mg + 20 wt.% SiC | 100 | 35 | 500 | 20 | 690 | [33] |
|
|