Effects of Milling Atmosphere and Increasing Sintering Temperature on the Magnetic Properties of Nanocrystalline Ni_0.36Zn_0.64Fe₂O₄

Figure 7

Coercivity versus sintering temperature from 500 to 900°C for Ni_0.36Zn_0.64Fe₂O₄ ferrite.