Effects of Milling Atmosphere and Increasing Sintering Temperature on the Magnetic Properties of Nanocrystalline Ni<sub>0.36</sub>Zn<sub>0.64</sub>Fe<sub>2</sub>O<sub>4</sub>

<div>The effects of grain size on coercivity in the samples sintered from 500 to 900°C.</div>

Journal of Nanomaterials

fig8

Figure 8

Figure 8: Effects of Milling Atmosphere and Increasing Sintering Temperature on the Magnetic Properties of Nanocrystalline Ni<sub>0.36</sub>Zn<sub>0.64</sub>Fe<sub>2</sub>O<sub>4</sub> 

Journal of Nanomaterials

Effects of Milling Atmosphere and Increasing Sintering Temperature on the Magnetic Properties of Nanocrystalline Ni0.36Zn0.64Fe2O4

Figure 8

Effects of Milling Atmosphere and Increasing Sintering Temperature on the Magnetic Properties of Nanocrystalline Ni_0.36Zn_0.64Fe₂O₄