Fabrication and Properties of High-Content Keratin/Poly (Ethylene Oxide) Blend Nanofibers Using Two-Step Cross-Linking Process
Table 2
The weight loss and range of temperatures with different stages in the TG curves of different samples.
| | Untreated nanofiber mat | First cross-linking nanofiber mat | Second cross-linking nanofiber mat | | Temperature (°C) | Weight loss (%) | Temperature (°C) | Weight loss (%) | Temperature (°C) | Weight loss (%) |
| Phase I | 20–111 | 8.05 | 22–127 | 3.98 | 36–127 | 1.96 | Phase II | 111–154 | 21.01 | 127–211 | 5.35 | 127–229 | 7.15 | Phase III | 154–258 | 36.66 | 211–384 | 36.77 | 229–384 | 49.6 | Phase IV | 258–346 | 12.18 | 384–445 | 12.41 | 384–447 | 12.30 |
|
|