Space Charge Property of Polyethylene/Silica Nanocomposites at Different Elongations
Figure 2
Accumulative characteristics of space charge (con represents concentration and elo represents elongation).
(a) LDPE |
(b) LDPE with elongation of 3% |
(c) LDPE with elongation of 6% |
(d) 15 nm; con is 3 wt% |
(e) 15 nm; con is 3 wt% and elo is 3% |
(f) 15 nm; con is 3 wt% and elo is 6% |
(g) 50 nm; con is 3 wt% |
(h) 50 nm; con is 3 wt% and elo is 3% |
(i) 50 nm; con is 3 wt% and elo is 6% |
(j) 15 nm; con is 5 wt% |
(k) 15 nm; con is 5 wt% and elo is 3% |
(l) 15 nm; con is 5 wt% and elo is 6% |
(m) 50 nm; con is 5 wt% |
(n) 50 nm; con is 5 wt% and elo is 3% |
(o) 50 nm; con is 5 wt% and elo is 6% |