Synthesis of FeNi Alloy Nanomaterials by Proteic Sol-Gel Method: Crystallographic, Morphological, and Magnetic Properties
Table 2
Magnetic properties of alloy synthesized with 50 mL/min and treated at 600 and 700°C.
| Mössbauer spectroscopy |
| | 600°C - 50 mL/min (H2) | | Singlet | Sextet | Hyperfine field | — | 31.49 T | Isomer shift | −0.120 mm/s | −0.078 mm/s | Quadrupole splitting | — | −0.007 mm/s | Area | 2.0% | 98.0% |
| Vibrating sample magnetometry |
| | 600°C - 50 mL/min (H2) | 700°C - 50 mL/min (H2) | Magnetization saturation | 113.35 emu/g | 141.33 emu/g | Remnant magnetization | 21.03 emu/g | 19.09 emu/g | Coercivity field | 262.77 Oe | 188.08 Oe |
|
|