Research Article
Dielectric Properties of Paper Made from Pulps Loaded with Ferroelectric Particles
Table 3
Tensile properties of ceramic loaded handsheets.
| Agave | Halfa | Pennisetum | Junc | Typha | Kraft | TMP | % | ME | | % | ME | | % | ME | | % | ME | | % | ME | | % | ME | | % | ME | |
| SrTiO3 (%: percentage, ME: modulus of elasticity (MPa), and : Young’s modulus (MPa)) | 15.3 | 738.8 | 808.5 | 11.3 | 455.8 | 488.3 | 9.7 | 835.1 | 894.9 | 7.9 | 715.7 | 754.2 | 9.8 | 1446.0 | 1500.4 | 7.7 | 833.2 | 870.34 | 11.8 | 954.2 | 1003.22 | 20.4 | 654.9 | 679.0 | 19.8 | 298.2 | 358.8 | 21.4 | 717.4 | 769.5 | 21.5 | 576.4 | 613.8 | 21.7 | 1412.0 | 1443.5 | 17.9 | 712.7 | 772.96 | 19.9 | 917.2 | 940.1 | 27.7 | 479.8 | 509.4 | 24.7 | 417.2 | 452.5 | 31.1 | 685.8 | 750.8 | 28.6 | 612.8 | 652.0 | 24.5 | 1144.0 | 1186.6 | 27.5 | 509.3 | 562.7 | 27.1 | 831.5 | 885.3 | 35.7 | 443.0 | 466.1 | 37.3 | 328.3 | 370.7 | 37.9 | 549.0 | 594.5 | 38.4 | 513.9 | 552.1 | 41.0 | 1034.0 | 1097.4 | 33.2 | 514.58 | 555.74 | 31.4 | 828.6 | 865.7 |
| BaTiO3 (%: percentage, ME: modulus of elasticity (MPa), and : Young’s modulus (MPa)) | 12.6 | 650.5 | 712.6 | 9.2 | 425.8 | 453.6 | 11.5 | 868.3 | 927.9 | 10.2 | 671.7 | 723.5 | 11.8 | 1441.0 | 1524.9 | 8.5 | 743.0 | 793.9 | 7.5 | 993.5 | 1030.5 | 18.7 | 587.6 | 619.5 | 18.2 | 381.4 | 422.8 | 18.6 | 811.2 | 857.3 | 20.1 | 669.1 | 710.9 | 22.2 | 1226.0 | 1334.7 | 15.5 | 773.9 | 826.6 | 19.4 | 972.1 | 1025.8 | 29.5 | 577.5 | 616.6 | 24.1 | 341.3 | 376.9 | 27.0 | 816.8 | 883.4 | 27.3 | 596.6 | 631.6 | 22.7 | 1295.0 | 1385.7 | 22.8 | 715.0 | 745.7 | 27.1 | 910.1 | 973.7 | 35.4 | 573.8 | 598.6 | 31.2 | 322.2 | 360.8 | 32.1 | 794.5 | 827.1 | 37.6 | 587.9 | 628.8 | 38.1 | 1126.0 | 1180.7 | 30.5 | 628.1 | 663.3 | 33.0 | 941.6 | 996.4 |
|
|