Nanoporous Glasses for Nuclear Waste Containment
Table 1
Normalized Ce, Nd, and Si mass loss (g⋅m−2) versus corrosion time.
| Days | SiO2 | SiO2-CeO2 | SiO2-CeO2 | SiO2-Nd2O3 | SiO2-Nd2O3 | Si mass loss (g⋅m−2) | Si mass loss (g⋅m−2) | Ce mass loss (g⋅m−2) | Si mass loss (g⋅m−2) | Nd mass loss (g⋅m−2) |
| 7 | 0.124 | 0.250 | n.m. | 1.17 | 0.01 | 14 | 0.252 | 0.436 | n.m. | 2.89 | 0.025 | 21 | 0.34 | 0.656 | 0.108 | 5.91 | 0.15 | 28 | 0.442 | 1.012 | 0.162 | 9.33 | 0.31 |
|
|