Catalytic Synthesis of Substrate-Free, Aligned and Tailored High Aspect Ratio Multiwall Carbon Nanotubes in an Ultrasonic Atomization Head CVD Reactor

<div>High aspect ratio MWCNTs synthesized at (a) SEM image at H<sub>2</sub> and Ar flow rates 3 and 1 L/min, temperature 800°C, and feed reaction time 30 min, (b) SEM image at H<sub>2</sub> and Ar flow rates 3 and 1 L/min, temperature 850°C, and feed reaction time 30 min, and (c) pure H<sub>2</sub> flow rate 4 L/min with no carrier gas, temperature 850°C, and reaction time 30 min.</div>

Journal of Nanomaterials

fig14

Figure 14

Figure 14: Catalytic Synthesis of Substrate-Free, Aligned and Tailored High Aspect Ratio Multiwall Carbon Nanotubes in an Ultrasonic Atomization Head CVD Reactor 

Figure 14 | Catalytic Synthesis of Substrate-Free, Aligned and Tailored High Aspect Ratio Multiwall Carbon Nanotubes in an Ultrasonic Atomization Head CVD Reactor 