Three-Dimensional Zn0.5Cd0.5S/Reduced Graphene Oxide Hybrid Aerogel: Facile Synthesis and the Visible-Light-Driven Photocatalytic Property for Reduction of Cr(VI) in Water
Figure 5
(a–c) SEM images of Zn0.5Cd0.5S/RGO aerogel at different magnifications; the inset in (a) is the digital photograph of a monolithic Zn0.5Cd0.5S/RGO aerogel. (d) EDS spectrum of Zn0.5Cd0.5S/RGO aerogel. (e) The result of elemental contents of C, Zn, Cd, and S contained in Zn0.5Cd0.5S/RGO aerogel, which was obtained from the EDS spectrum shown in (d). (f–i) EDS elemental mapping images of C, Zn, Cd, and S within Zn0.5Cd0.5S/RGO aerogel, suggesting their uniform distribution in the sample. (j and k) TEM images of Zn0.5Cd0.5S/RGO aerogel at low and high magnifications, respectively. (l) HRTEM image of an individual Zn0.5Cd0.5S solid solution nanocrystal trapped in the matrix of Zn0.5Cd0.5S/RGO hybrid aerogel, showing its (111) lattice plane.