Poly-γ-Glutamic Acid Nanoparticles Based Visible Light-Curable Hydrogel for Biomedical Application
Table 2
Mechanical parameters of MPGA hydrogels and PGA nanogels.
| | Compressive strain at break (mm/mm) | Compressive stress at break (MPa) | Young’s modulus (MPa) |
| MPGA hydrogel | 0.452 ± 0.086 | 1.484 ± 0.503 | 4.321 ± 1.364 | PGA nanogel | 0.529 ± 0.124 | 0.730 ± 0.363 | 0.926 ± 0.433 |
|
|