Improved Bonding Strength of Hydroxyapatite on Titanium Dioxide Nanotube Arrays following Alkaline Pretreatment for Orthopedic Implants

<div>SEM images of HA coating on different ATi (without 0.5 M NaOH pretreatment) which were anodized under different conditions: (a) at 5°C, +20/−4 V; (b) at 5°C, +35/−4 V; (c) at 25°C, +20/−4 V; and (d) at 25°C, +35/−4 V for 90 minutes. Scale bars are 5 <i>μ</i>m. Black arrows represent HA crystal thickness. Inset graphs are thickness analysis of HA using ImageJ. Data are calculated from three SEM images with <svg height="8.55521pt" id="M13" style="vertical-align:-0.2063904pt" version="1.1" viewbox="-0.0498162 -8.34882 34.1002 8.55521" width="34.1002pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M495 86L479 114C446 82 419 66 409 66C401 66 401 72 406 97C420 166 436 231 453 297C489 435 454 448 428 448C406 448 384 439 354 422C305 394 222 327 161 247H159L183 345C200 415 194 448 173 448C143 448 82 410 23 351L38 325C64 349 95 371 105 371C111 371 116 365 109 336L25 -4L31 -12C50 -4 77 3 107 9C119 69 132 122 145 168C197 254 321 381 370 381C387 381 393 374 378 305L329 95C309 17 320 -12 345 -12C372 -12 430 19 495 86Z" id="g113-111"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="502" vert-adv-y="502"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,10.158,0)"><path d="M535 323V373H52V323H535ZM535 138V188H52V138H535Z" id="g117-34"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="587" vert-adv-y="587"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,21.421,0)"><path d="M285 378C315 398 338 416 353 432C373 451 384 474 384 503C384 579 325 635 236 635H235C182 635 136 610 108 579L65 516L85 496C110 533 150 575 205 575C258 575 300 543 300 481C300 407 232 369 141 339L147 310C163 315 188 321 211 321C268 321 338 284 338 192C338 94 288 40 217 40C160 40 119 68 93 91C85 98 77 97 69 91C60 84 47 71 46 58C44 46 48 35 62 22C75 10 116 -12 162 -12C234 -12 424 62 424 224C424 297 373 359 285 376V378Z" id="g113-52"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,27.661,0)"><path d="M241 635C89 635 35 457 35 312C35 153 89 -12 240 -12C390 -12 443 166 443 312C443 466 390 635 241 635ZM238 602C329 602 354 454 354 312C354 172 330 22 240 22C152 22 124 173 124 313S148 602 238 602Z" id="g113-49"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g></svg>.</div>

Journal of Nanomaterials

fig3

Figure 3

Figure 3: Improved Bonding Strength of Hydroxyapatite on Titanium Dioxide Nanotube Arrays following Alkaline Pretreatment for Orthopedic Implants 