Preparation of Cerium Dioxide Layers on Titanium by Electrodeposition with Organic Solution

Table 2

Estimated crystallite size (Scherrer size), lattice parameter , dislocation density δ, strain, stacking fault (SF), and texture coefficient (TC) of two CeO₂ samples electrodeposited on Ti which were as prepared and calcined at 700 K for 30 min.

CeO2 sample		Scherrer size (nm)	(Å)	δ; (nm^−2)	Strain	SF	TC
As-prepared	111	3.630	5.441	0.07587	0.00955	0.01983	1.1899
	200	4.146	5.439	0.05817	0.00836	0.01628	0.8344
	220	4.049	5.451	0.06098	0.00856	0.01432	1.1136
	311	3.175	5.424	0.09918	0.01092	0.01714	0.8622
Calcined at 700 K for 30 min	111	6.991	5.428	0.02046	0.00496	0.01029	1.1364
	200	8.494	5.426	0.01386	0.00408	0.00792	0.9499
	220	6.572	5.420	0.02315	0.00527	0.00880	1.0453
	311	6.612	5.420	0.02287	0.00524	0.00823	0.8685