Effect of Microstructural Changes during Annealing on Thermoelectromotive Force and Resistivity of Electrodeposited Ni_85.8Fe_10.6W_1.4Cu_2.2 Alloy

Table 1

Microstructural data for the crystalline FCC phase of Ni_85.8Fe_10.6W_1.4Cu_2.2 alloy: (A) as-deposited and (B) annealed for 60 minutes at 600°C.

	Unit cell parameters (nm)	Mean crystallite size value (nm)	Mean microstrain value	Minimum density of chaotically distributed dislocations (cm^−2)
(A)	= 0.35324 ()	11.4 ()	1.3 () · 10^3	2.0 () · 10^12
(B)	= 0.35950 ()	24.1 ()	0.3 () · 10^3	0.08 () · 10^12