Lanthanum-Based Perovskite-Type Oxides La1−xCexBO3 (B = Mn and Co) as Catalysts: Synthesis and Characterization
Table 3
XPS peak positions and atomic percentages of
and
perovskites obtained from the fitting of La 3d, Co 3p, Mn 3p, Ce 3d, and O1s XPS spectra.
| | LaCoO3 | La0.8Ce0.2CoO3 | La0.6Ce0.4CoO3 | LaMnO3 | La0.8Ce0.2MnO3 |
| La 3d (eV) | 834.3 | 834.7 | 834.3 | 834.7 | 834.4 | 850.9 | 851.8 | 851.1 | 851.7 | 851.1 | Co 3p/Mn 3p (eV) | 779.9 | 780.2 | 779.9 | 641.8 | 641.8 | 795.2 | 795.8 | 795.5 | 653.1 | 653.2 | O 1s (eV) | 528.5 | 528.8 | 528.7 | 528.8 | 528.9 | 531.4 | 531.6 | 531.5 | 531.4 | 531.5 | Ce1 (at. %) | — | 4.84 (3.9) | 7.11 (3.6) | — | 6.4 (10.1) | O (at. %) | 75.1 | 73.6 | 73.4 | 77.4 | 74.9 | La (at. %) | 15.7 | 13.2 | 11.2 | 17.2 | 14.2 |
|
|
value in parenthesis is a peak percentage (%) of the Ce3+ ion.
|