PLA-Based Hybrid and Composite Electrospun Fibrous Scaffolds as Potential Materials for Tissue Engineering
Table 1
Characterisation of fibrous mats.
| Type | Fibre diameter, (nm) | Material porosity, | Wettability, (°) | Tensile strength, (MPa) | Young’s modulus, (MPa) |
| PLA | 1029 ± 36 | 0.93 ± 0.01 | 113.3 ± 1.0 | 10.6 ± 0.4 | 686 ± 42 | PLA/GEL | 400–1250 | 0.88 ± 0.01 | 53.2 ± 1.9 | 4.1 ± 0.6 | 459 ± 105 | PLA + CNT | 306 ± 17 | 0.89 ± 0.01 | 108.3 ± 1.4 | 16.3 ± 2.0 | 1054 ± 112 | PLA + CNT/GEL | 300–770 | 0.87 | 51.4 ± 1.4 | 12.3 ± 1.9 | 898 ± 91 |
|
|
Two-component fibre distribution.
|