Tribomechanical Properties of a Carbon-Based Nanolayer Prepared by Nitrogen Ion Beam Assisted Deposition for Finger Joint Replacements
Table 2
The results of Raman spectra.
| | Peak no. |
| | 1 | 2 | 3 | | Layer type | Peak position (cm−1) | Intensity (a.u.) | Peak position (cm−1) | Intensity (a.u.) | Peak position (cm−1) | Intensity (a.u.) | Ratio I(1 + 2)/I3 |
| IBAD 20 nm | 1127 ± 15 | (0.818 ± 0.016)E6 | 1385 ± 16 | (4.653 ± 0.044)E6 | 1565 ± 13 | (1.629 ± 0.012)E6 | 3.36 | IBAD 40 nm | 1150 ± 16 | (0.721 ± 0.008)E6 | 1402 ± 19 | (4.577 ± 0.009)E6 | 1565 ± 12 | (1.672 ± 0.010)E6 | 3.17 | C 40 nm | 1123 ± 11 | (0.539 ± 0.006)E6 | 1394 ± 10 | (4.286 ± 0.011)E6 | 1567 ± 18 | (1.564 ± 0.009)E6 | 3.09 |
|
|