Magneto-Optic Properties of Ultrathin Nanocrystalline Ferrite Garnet Films in the 8K to 300K Temperature Interval
Figure 2
(a) AFM surface relief scan of an annealed ultrathin ferrite garnet film of nominal composition Bi2Dy1Fe4Ga1O12 and 1.7 nm thickness, deposited onto a GGG substrate. (b) Partial surface scan data from a flatter part of scan shown in (a). The larger nanocrystallites’ height reaches 5 nm. (c) Surface relief profile measured along a scanned line in a garnet film of nominal composition Bi2Dy1Fe4Ga1O12 and 1.7 nm thickness and (d) starting 400 nm-long part of the line scan profile shown in (c).