Magneto-Optic Properties of Ultrathin Nanocrystalline Ferrite Garnet Films in the 8K to 300K Temperature Interval

Figure 8

MCD spectral dependencies measured in a 1.7 nm-thick sample of iron garnet film between 200 K and 8 K (the signal was also at zero level at 300 K). The sensitivity of dichroghraph scale was 2 × 10⁻⁶.