Effects of Biceramic AlN-SiC Microparticles on the Thermal Properties of Paraffin for Thermal Energy Storage
Table 1
Specifications of as-received materials.
| Material | Average particle size (μm) | (g/cm3) at 25°C [18] | (W/m·K) at 25°C | (J/kg·K) at 0–100°C | Melting point (°C) [18] |
| Paraffin wax | — | 0.90 | <0.4 [19] | 2140–2900 [20] | 53–57 (ASTM D87) | Aluminium nitride (AlN) | 6.0 | 3.26 | 320 [21] | 819.7 [22] | >2200 | Silicon carbide (SiC) | 67.8 | 3.22 | 270 [21] | 675.4 [23] | 2700 |
|
|