Morphology and Electrochemical Characterization of Electrodeposited Nanocrystalline Ni-Co Electrodes for Methanol Fuel Cells
Table 4
Corrosion properties of nanocrystalline electrodeposited Ni-Co alloys and the steel substrate in 1 M methanol + 0.5 M H2SO4.
| Time (min) | | | (mV) | (μA/cm2) | Corrosion rate (μm/y) | (KΩ) |
| 30 mA/cm2 | 15 | 40.5 | 37.5 | −205.9 | 6.64 | 71.59 | 1.12 | 20 | 47.7 | 48 | −162 | 5.93 | 63.95 | 3.27 | 30 | 37.7 | 33 | −156.1 | 5.04 | 54.33 | 1.99 | 50 mA/cm2 | 15 | 24.9 | 41.6 | −188 | 5.61 | 60.53 | 0.999 | 20 | 25.9 | 42.8 | −104 | 4.71 | 50.78 | 1.240 | 30 | 27.6 | 36.7 | −97.4 | 3.40 | 36.73 | 1.540 | 80 mA/cm2 | 15 | 27.4 | 40 | −116 | 3.53 | 38.11 | 1.95 | 20 | 17.1 | 31.6 | −85 | 2.47 | 26.73 | 0. 846 | 30 | 10.4 | 29.2 | −52.2 | 2.37 | 25.62 | 1.82 | Stainless steel substrate | — | 13.58 | 34.2 | −231 | 1.53 | 11.73 | 8.36 |
|
|