Morphology and Electrochemical Characterization of Electrodeposited Nanocrystalline Ni-Co Electrodes for Methanol Fuel Cells
Table 5
The EIS results of all electrodeposited nanocrystalline Ni-Co alloys tested in 1 M methanol + 0.5 M H2SO4.
| Time (min) | (KΩ) | (Ω) | (μF/cm2) | |
| 30 mA/cm2 | 15 | 1.82 | 7.917 | 63.5 | 0.88 | 20 | 3.09 | 7.178 | 63.3 | 0.86 | 30 | 2.39 | 7.714 | 35.9 | 0.86 | 50 mA/cm2 | 15 | 7.99 | 7.425 | 15.6 | 0.85 | 20 | 2.64 | 7.31 | 18.8 | 0.86 | 30 | 1.71 | 6.969 | 22.8 | 0.89 | 80 mA/cm2 | 15 | 3.6 | 7.137 | 51.8 | 0.843 | 20 | 2.27 | 6.916 | 27.8 | 0.845 | 30 | 2.53 | 7.122 | 37.5 | 0.814 | Stainless steel substrate | — | 103 | 7.271 | 42. 9 | 0.89 |
|
|