Review Article
Recent Progress on Mg- and Zn-Based Alloys for Biodegradable Vascular Stent Applications
Table 4
Recently reported processing and properties of wrought Zn alloys.
| Alloys | Processes | Dimensions | YS (MPa) | UTS (MPa) | EL (%) |
| Zn-0.15Mg [48] | DE+TE | Tube: outer diameter of 4 mm; inner diameter of 1.5 mm | 114 | 250 | 22 | Zn-0.5Mg [48] | 159 | 297 | 13 | Zn-1Mg [48] | 180 | 340 | 6 | Zn-3Mg [48] | 291 | 399 | 1 | Zn-1Mg-1Ca [49] | HR HE | — | 210 | 260 | 5.5 | Zn-1Mg-1Sr [49] | 200 | 250 | 7.5 | Zn-1Ca-1Sr [49] | 215 | 265 | 6.8 | Zn-1Mg-0.1Sr [50] | HR | Sheet metal: thickness of 2.1 | 196 | 300 | 22.49 | Zn-1Mg-0.1Mn [51] | | Sheet metal: thickness of 2.1 | 195 | 299 | 26.07 | Zn-1Ca [52] | HE | Rod: diameter of 10 mm | 195 | 240 | 7.5 | Zn-1Sr [52] | 220 | 260 | 10.8 | Zn-1Mg [52] | 205 | 265 | 8.5 | Zn-0.5Al [48] | DE+TE | Tube: outer diameter of 4 mm; inner diameter of 1.5 mm | 119 | 203 | 33 | Zn-1Al [48] | 134 | 223 | 24 | Zn-1Cu [15] | HE | Rod: diameter of 20 mm | 149 | 186 | 21 | Zn-2Cu [15] | 199 | 240 | 46.8 | Zn-3Cu [15] | 213 | 257 | 47.2 | Zn-4Cu [15] | 227 | 270 | 50.6 | Zn-3Cu-0.1Mg [53] | HE | Rod: diameter of 20 mm | 340 | 375 | 5 | Zn-3Cu-0.5Mg [53] | 400 | 425 | 2 | Zn-3Cu-1Mg [53] | 425 | 450 | 1 | Zn-2.5Ag [54] | HE | Rod: extrusion ratio of 14 : 1 | 155 | 205 | 35 | Zn-5.0Ag [54] | 210 | 260 | 38 | Zn-7.0Ag [54] | 240 | 290 | 32 |
|
|
DE: direct extrusion; TE: tube extrusion; HE: hot extrusion; HR: hot rolling. |