Electrode Composite LiFePO4@Carbon: Structure and Electrochemical Performances
Table 1
Summary of composite electrode LiFePO4@carbon prepared by hydrothermal method.
| Authors | Hydrothermal condition | Grain’s size | Temperature pyrolysis | Capacity |
| Brochu et al. [13] | 185°C for 2 hours | 240 nm thick and 1 μm length | 650°C for 2 hours in argon | 160 mAh/g at rate C/10 | Chen et al. [14] | 200°C for 6 hours | 2-3 μm | 600°C for 2 hours in argon | 150 mAh/g at rate C/10 | Lim et al. [15] | 240°C from 2 to 36 hours | 300–600 nm | | 180 mAh/g (50 cycles) at rate C/10 | Jiang et al. [16] | 180°C for 2 hours | | 700°C for 6 hours in argon | 160 mAh/g (100 cycles) at rate C/10 | Zhan et al. [17] | 180°C for 12 hours | 2-3 μm | 550°C for 4 hours in argon | 150 mAh/g (50 cycles) at rate C/5 |
|
|