Preparation and Properties of Nanocellulose from Miscanthus x giganteus Table 1 Dependencies of the parameters of nanocellulose films on the main technological parameters of the process of obtaining nanocellulose from organosolvent miscanthus pulp.
Concentration H2 SO4 (%) Duration of hydrolysis (min) Duration of ultrasonic treatment (min) Quality of received films Density (g/cm3 ) Tensile strength (MPa) Transparency (%) Temperature 40°С 43/50 30 30 0.87/1.00 56.0/44.2 25.8/57.0 45 1.04/1.08 58.3/54.1 40.6/64.2 60 1.05/1.12 80.0/66.7 41.8/67.0 60 30 1.04/1.12 54.5/50.0 30.3/51.1 45 1.08/1.15 59.3/66.1 43.3/67.0 60 1.16/1.22 77.7/83.3 52.769.7 90 30 1.09/1.15 70.7/77.5 42.7/59.9 45 1.11/1.18 83.3/105.0 54.5/64.3 60 1.18/1.23 124.0/127.0 55.6/69.3 Temperature 60°С 43/50 30 30 1.12/1.1 43.3/66.7 44.3/65.7 45 1.22/1.23 57.5/70.7 52.0/75.6 60 1.26/1.28 60.4/75.0 70.7/76.3 60 30 1.15/1.33 55.5/78.0 68.6/68.7 45 1.23/1.37 60.0/80.6 65.3/70.9 60 1.32/1.42 62.0/88.0 74.4/80.8 90 30 1.04/1.45 44.4/115.0 38.5/75.7 45 1.18/1.55 40.0/123.0 68.2/78.0 60 1.25/1.60 41.0/195.0 72.3/82.6