Theoretical Modelling Analysis on Tensile Properties of Bioepoxy/Clay Nanocomposites Using Epoxidised Soybean Oils
Table 3
Percentage errors in theoretical models in comparison with experimental data at different clay contents in bionanocomposites.
| Theoretical model | Percentage error (%) | Clay content (wt%) | 1 | 3 | 5 | 8 |
| Voigt | 79.54 | 259.82 | 428.63 | 809.72 | Voigt (MRF) | 46.25 | 163.54 | 273.55 | 527.57 | Reuss | -17.25 | -20.11 | -22.19 | -10.41 | Hirsch | -14.47 | -12.09 | -9.27 | 13.10 | H-T laminate random | 2.75 | 1.95 | 3.27 | 8.66 | H-T laminate random with MRF | -1.98 | -0.74 | 2.73 | 2.28 | Modified H-T random | 0.71 | -2.40 | 6.59 | 5.85 | Modified H-T random with MRF | -0.91 | -2.03 | -2.46 | 0.85 | H-S laminate | -1.60 | -3.48 | -1.84 | -0.07 |
|
|
Note: Negative values in percentage errors represent lower prediction values than experimental data.
|