Theoretical Modelling Analysis on Tensile Properties of Bioepoxy/Clay Nanocomposites Using Epoxidised Soybean Oils

Table 5

Tensile properties of blend matrices and effective moduli of intercalated clay particles in bionanocomposites (fixed clay content: 5 wt%).

ESO content				Bionanocomposites at a fixed clay content of 5 wt%
(wt%)	GPa	MPa	g·cm^-3	[56] (nm)	(GPa)
0	3.30	59.56	1.17	1.80	92.72
20	0.49	28.53	1.13	1.96	85.59
40	0.13	10.26	1.09	2.07	80.65
60	1x10^-4	0.29	1.06	1.97	85.08